Range of Polymer Composite Products

uPVC| WPC based Composite Interior & Exterior Products For Residential, Commercisl & Workplace

10 Resons to select

Sr.No. Test Tests Method Test Result
1 Density Kg/m3 IS: 2380 (P-3) 1997 650+
2 Moisture Content, % IS: 2380 (P-3) 1997 0.3
3 Water Absorption, %
a) 2 Hours
b) 24 Hours
IS: 2380 (P-16) 1997
0.14
0.5 
4 Thickness swelling, %
After 2 hours
IS: 2380 (P-17) 1997 0.2
5 Modulus of rupture N/mm2 IS: 2380 (P-4) 1997 More than 19.6
6 Modulus of Elasticity, N/mm2 IS: 2380 (P-4) 1997 1957
7 Tensile Strength, N/mm2 IS: 2380 (P-6) 1997 12.5
8 Screw withdrawal strength N
a) Face
b) Edge
IS: 2380 (P-14) 1997
1574 
970
9 Nail withdrawal strength N
a) Face
b) Edge
IS: 2380 (P-14) 1997
1224
982 
10 Screw holding test IS: 2380 (P-14) 1997 Satisfactory
11 Nail holding test IS: 2380 (P-14) 1997 Satisfactory
12 Flexure test IS: 4020(P-5)1998 Passes the test
13 Edge loading test IS: 4020(P-6)1998 Passes the test
14 Shock resistance test (5 kgf) IS: 4020(P-7)1998 Passes the test
15 Water resistance test (5 kgf) IS: 4020(P-4)1998 Passes the test
16 Knife test IS: 4020(P-13)1998 Passes the test
17 Resistance to stain IS: 12823:1990 Passes the test
18 Resistance to crack IS: 12823:1990 Passes the test
19 Resistance to steam IS: 12823:1990 Passes the test
20 Resistance to cigarette burn IS: 12823:1990 Passes the test
21 Spot test IS: 1659:2004 Passes the test
22 Mycological test IS: 1734(P-7):1983 Passes the test
23 Humidity test (varying)
At 27± 2°C & 30 ± 5% RH (for one week)
27± 2°C & 85 ± 5% RH (for one week
)(size : 300 X 300 mm)
IS: 4020(P-11):1983
Guideline
Length-0.06mm
Thick-0.02mm
24 Thickness, mm IS:2380(P-2):1977 12.06
25 Squareness, mm IS:2380(P-2):1977 0.04
26 Edge Straightness test, mm IS:2380(P-2):1977 0.04
27 Retention of Preservation   Passes the test
28 Softning Point, °C   118
29 Heat deflection temp, °C= IS:1734(P-2) 134
30 Work Ability Test   Satisfactory
31 Fire point °C   384